产品详情
1/4" -30℃ | ASTM D256/ISO 179 | 15 | kg·cm/cm(J/M)ft·lb/in | |
1/8" 23℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | ||
1/8" -30℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | ||
Charpy冲击强度 | 23℃ (缺口) | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |
-30℃(缺口) | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | ||
23℃(无缺口) | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | ||
-30℃(无缺口) | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | ||
拉伸断裂伸长率(延伸率) | ASTM D638/ISO 527 | >50 | % | |
物性性能 | 测试条件 | 测试方法 | 数值/述 | 单位 |
---|---|---|---|---|
比重(密度) | ASTM D792/ISO 1183 | 1200 | ||
成型收缩率 | ASTM D955 | 0.6-0.8 | % | |
熔融指数(流动系数) | 200℃/5kg | ASTM D1238/ISO 1133 | g/10min | |
220℃/10kg | ASTM D1238/ISO 1133 | 10 | g/10min | |
吸水率 23℃/24H | ASTM D570/ISO 62 | 0.35 | % | |
热性能 | 测试条件 | 测试方法 | 数值/描述 | 单位 |
热变形温度 | 退火 | ASTM D648/ISO 75 | ℃(℉) | |
未退火 | ASTM D648/ISO 75 | ℃(℉) | ||
维卡软化点 | ASTM D1525/ISO R306 | 144 | ℃(℉) | |
熔点 | - | ℃(℉) | ||
燃烧性(率) | UL94 | V-2 | ||
线性膨胀系数 | ASTM D696/ISO 11359 | 0.7 | mm/mm.℃ |